W-5 is a classical, reduced-gold ceramic alloy. The good casting characteristics and the high heat resistance allow for the production ceramic veneered to metal frameworks and implant-supported superstructures of high accuracy.
Indications*
- Onlays, ¾ crowns, crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Au 52.2 | Pd 26.0 | Ag 17.1 | Sn 2.7 | Pt <1.0, In <1.0, Ir <1.0, Re <1.0, Li <1.0 |
| ISO | 22674:2016 |
| ADA Class: | High Noble |
| Type / Color: | 4 / White |
| Density (g/cm³) | 13.8 |
| Melting Range (Solidus/Liquidus): | 1185 - 1285 °C |
| Elastic Modulus (GPa): | 130 |
| Porcelain Fired Hardened | |
| Vickers Hardness: | 215 255 |
| Tensile Strength (MPa): | 715 745 |
| 0.2% Proof Stress (MPa): | 475 520 |
| Elongation (%): | 15 12 |