BioUniversal E is a copper-free, universal alloy, which can be used for a wide range of indications. Due to its low density, this alloy is suitable for the production of economical restorations and can be veneered with low-fusing special ceramics.
Indications*
- Onlays, 3/4 crowns, crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
Technical Data
| Composition (%): | Ag 52.2 | Pd 40.0 | Sn 5.5 | In 1.4 | Zn <1.0, Re <1.0, Ru <1.0 |
| ISO | 22674:2016 |
| ADA Class | Noble |
| Type / Color | 4 / White |
| Density (g/cm³) | 10.9 |
| Melting Range (Solidus/Liquidus): | 1100 - 1180 °C |
| Elastic Modulus (GPa): | 127 |
| As Cast Porcelain Fired Hardened | |
| Vickers Hardness: | 200 190 220 |
| Tensile Strength (MPa): | 600 550 645 |
| 0.2% Proof Stress (MPa): | 395 360 425 |
| Elongation (%): | 10 10 6 |
Advantages
- Economical use due to low density
- Easy processing and polishing
- Good melting and flow properties
- Compatible with various special ceramics and composite veneering materials
- Tested biocompatibility
Processing Data
| Investment Material: | Phosphate-bonded / Gypsum-bonded |
| Preheating / Burn- out Temperature: | 650 - 760 °C |
| Crucible | Ceramic crucible |
| Casting Temperature: | 1240 - 1290 °C |
| Oxidation °C/min/Vacuum: | 800 / 5 / No |
| CTE: | (25 – 500 °C): 16.1 x 10-6 /K |
| Laser Welding Wire: | Laser C&B White |
*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES