Callisto Implant 60 is a palladium-based ceramic alloy. The high strength and the low density make this alloy economical to use, especially for implant-supported superstructures.
Indications*
- Onlays, ¾ crowns, crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Pd 60.0 | Ag 25.2 | Sn 7.5 | Au 2.0 | In 2.0 | Zn 1.6 | Ga 1.0 | Pt <1.0, Re <1.0 |
| ISO | 22674:2016 |
| ADA Class | Noble |
| Type / Color | 4 / White |
| Density (g/cm³) | 10.8 |
| Melting Range (Solidus/Liquidus): | 1150 - 1260 °C |
| Elastic Modulus (GPa): | 140 |
| Porcelain Fired Hardened | |
| Vickers Hardness: | 275 260 |
| Tensile Strength (MPa): | 820 715 |
| 0.2% Proof Stress (MPa): | 590 620 |
| Elongation (%): | 18 12 |
Advantages
- High strength
- Economical due to low density
- High corrosion resistance
- Excellent milling properties
- Compatible with conventional metal-ceramics (e.g. IPS Style)
- Low melting range
Processing Data
| Investment Material: | Phosphate-bonded |
| Preheating / Burn- out Temperature: | 750 - 820 °C |
| Crucible | Ceramic crucible |
| Casting Temperature: | 1320 - 1360 °C |
| Oxidation °C/min/Vacuum: | 950/1/Nos |
| CTE: | (25 – 500 °C): 14.5 x 10-6 /K |
| Recommended Metal Ceramic: | IPS Style, IPS InLine One, IPS InLine, IPS Classic |
| Laser Welding Wire: | Laser Ceramic Yellow PdF |
*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES