Porta Maximum

Au (70.0%)-based dental casting/ metal-ceramic alloy, Type 4

Porta Maximum

Porta Maximum is a high gold, copper-free universal alloy. The constituents in this alloy allow for a wide range of indications, especially for the milling and double crown techniques.

Indications*

  • Inlays
  • Onlays, 3/4 crowns, crowns
  • Telescope crowns, conus crowns
  • Bridges
  • Wide-span bridges
  • Cast posts / cores, bars, attachments
  • Partial dentures

Technical Data

Composition (%):  Au 70.0 | Ag 10.0 | Pt 10.0 | In 5.0 | Pd 2.5 | Zn 2.0 | Rh <1.0 
ISO  22674:2016
Type / Color 4 / Rich Yellow
Density (g/cm³) 16.2
Melting Range (Solidus/Liquidus): 910 - 1060 °C
Elastic Modulus (GPa): 98
  As Cast              Porcelain Fired        Hardened 
Vickers Hardness: 180                      190                            210
Tensile Strength (MPa): 560                      580                            600
0.2% Proof Stress (MPa):  380                      410                            460
Elongation (%): 10                         8                               7

 