X-L

Au (61.7%)-based dental casting alloy, Type 4
Purchase Online Today

X-L

X-L is a gold-reduced casting alloy with a golden yellow colour. The coordinated material properties allow successful clinical use in various different areas of indication.

Indications*

  • Inlays
  • Onlays, ¾ crowns, crowns
  • Telescope crowns, conus crowns
  • Bridges
  • Wide-span bridges
  • Cast posts / cores, bars, attachments

Technical Data

Composition (%):  Au 61.7 | Pd 3.0 | Ag 25.2 | Cu 9.6 | In <1.0, Ir <1.0
ISO  22674:2016
ADA Type High Noble
Type / Color 4 / Yellow
Density (g/cm³) 14.0
Melting Range (Solidus/Liquidus): 890 - 950 °C
Elastic Modulus (GPa): 105
  As Cast              Softened        Hardened 
Vickers Hardness: 150                      125                  240
Tensile Strength (MPa): 500                      410                  660
0.2% Proof Stress (MPa):  390                      270                  515
Elongation (%): 26                        35                    18

Advantages

  • Golden yellow colour
  • Clinically proven
  • Wide range of indications
  • Tested biocompatibility

Processing Data

Investment Material:  Phosphate-bonded / Gypsum-bonded
Preheating / Burn- out Temperature: 650 - 760 °C
Crucible  Carbon crucible / Ceramic crucible
Casting Temperature: 1010 - 1070 °C
Laser Welding Wire: Laser C&B Yellow

*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES

Download Materials

Get this product in our online shop

Buy now in our Online Shop with your Ivoclar webshop account

Click here to go to the online shop